www.finnedtubes.cn | Site map | Contact | Download Catalogue | Print | Favorite | 中文magvant.cn
MAGVANT CHINA LIMITED
news
Home
Boiler tubes

Heat exchanger tubes

Welded pipes

L, LL, KLM finned tubes (fin tubes)

high frequency welded (serrated) finned tubes (fin tubes)

(serrated) extruded finned tubes

hot dipped galvanized oval (elliptical) finned tubes, rectangular fin tubes

condenser fin flat tubes

H / double H finned tubes (fin tubes)

Studded Pipes

Laser welded finned tubes (fin tubes)

G embedded finned tubes (fin tubes)

inner finned tubes (fin tubes)

longitudinal finned tubes (fin tubes)

seamless finned tubes with two longitudinal opposite fins

casting alloy tubes

Tube finning machine

Aluminum plates, strips,foils

Aluminum welding wire rod

Aluminum tubes, profile

Economizer for Boiler

air-cooled heat exchanger (air cooler)

material

standard & specification

 
ASTM A335 Pipe Specifications

ASTM A335 Standards specifications download

This specification covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding.

Grade P-5 P-9 P-11 P-22 P-91 P-91 shall also include the following:
Element UNS Designation K41545 S50400 K11597 K21590 K91560
Carbon 0.15 max 0.15 max 0.05 - 0.15 0.05 - 0.15 0.08 - 0.12 V at 0.18 - 0.25
Manganese 0.30 - 0.60 0.30 - 0.60 0.30 - 0.60 0.30 - 0.60 0.30 - 0.60 N at 0.030 - 0.070
Phosphorous, max 0.025 0.025 0.025 0.025 0.020 Ni at 0.40 max
Sulfur, max 0.025 0.025 0.025 0.025 0.010 Al at 0.02 max
Silicon 0.50 max 0.25 - 1.00 0.50 - 1.00 0.50 max 0.20 -0.50 Cb at 0.06 - 0.10
Chromium 4.00 - 6.00 8.00 - 10.00 1.00 - 1.50 1.90 - 2.60 8.00 - 9.50 Ti at 0.01 max
Molybdenum 0.45 -0.65 0.90 - 1.10 0.44 - 0.65 0.87 - 1.13 0.85 - 1.05 Zr at 0.01 max

Seamless
P-5 P-9 P-11 P-22 P-91 P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Tensile Strength, min., psi
ksi 60 60 60 60 85
MPa 415 415 415 415 585
Yield Strength, min., psi
ksi 30 30 30 30 60
MPa 205 205 205 205 415

P5, P9, P11, and P22
Grade Heat Treatment Type Normalizing Temperature Range F [C] Subcritical Annealing or Tempering
Temperature Range F [C]
P5 (b,c) Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
Subcritical Anneal (P5c only) ***** 1325 - 1375 [715 - 745]
P9 Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
P11 Full or Isothermal Anneal
Normalize and Temper ***** 1200 [650]
P22 Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
P91 Normalize and Temper 1900-1975 [1040 - 1080] 1350-1470 [730 - 800]
Quench and Temper 1900-1975 [1040 - 1080] 1350-1470 [730 - 800]

 